© 2015 Elsevier Ltd. All rights reserved. A pressure induced lattice expansion of Graphite Oxide (GO) in presence of <sup>NH3</sup> was observed by X-ray diffraction during room temperature compression and decompression up to 7 GPa in a diamond anvil cell (DAC). A remarkable increase (∼11%) of the interlayer d-spacing of GO was observed between 0.2 and 1.1 GPa in the liquid phase of <sup>NH3</sup>, indicating the occurrence of molecular insertion between the GO layers. The expansion is reversible with the release of pressure, thus leading to a pressure induced breathing of the GO lattice. The presence of high density <sup>NH3</sup> between the GO layers opens new perspectives for N-doping and chemical functionalization of GO and for designing new advanced carbon based nanostructured materials.